Fevicol PUR 150g

Pidilite Fevicol PUR Moisture Curing Polyurethane Adhesive

Product Description

Price is including GST @ 18 %COLOUR: Brownish Liquid

APPLICATION CONSISTENCY

Brush, Spatula, nozzle applicator

AVERAGE NON-VOLATILE (PIL method)

Not less than 99.5% by weight 

VISCOSITY (Brookfield RVT)

30-60 PS 

WATER RESISTANCE (DIN EN 204/D4) (Test report 505 32054/2e, dated August 2006, ift Rosenheim, Germany)

Confirms to German DIN standard for boiling water resistance.

HEAT RESISTANCE (WATT 91) (Test by ift Rosenheim, Germany)

Confirms to high heat resistance as per WATT91. Adhesive Strength 12.8 N/mm2

  COVERAGE RANGE (PSTM WI 1069)

  (Subject to type of surface coated)

   8.0 – 9.0 m2 /Kg

VOC - 1.0 g/L max

Fevicol 1K PUR is a one component ready to use moisture curing polyurethane adhesive with gap filling properties.

Fevicol 1K PUR adhesive is a very fast setting adhesive. Initial handling strength is achieved within 30 minutes.  

Fevicol 1K PUR adhesive is designed to adhere wood, MDF, fiberboard, particleboard, metal, laminates, stone, ceramic, brick, foam, fiberglass, marble, plasterboard, masonry, rubber, some plastics and many other substrates. 

Fevicol 1K PUR adhesive can be used in edge to edge joints, I- beam joints. It is suitable for bonding tropical wood, sandwich panels. Typical applications in window, door, pillar. It gives an exceptionally high mechanical strength.

Fevicol 1K PUR is specially designed for exterior weather condition. The adhesive bond is resistance to cold and hot weather conditions 

Fevicol 1K PUR gives a clear glue line on drying that can be sanded, painted or stained.

APPLICATION

By Brush/Roller/Spatula

Apply to one surface in a thin layer, assemble the parts and leave to set, it will set in 30mininutes. During cure this product will expand to fill gaps and rough surfaces, when foamed. Firmly clamp both the substrates. A strong bond will be obtained after 2 - 3 hours and full strength will be realized after 24 hours at room temperature. Individual substrates should be evaluated for bonding performance prior to any large scale application.

MATERIAL PREPARATION

Surface to be bonded should be dry, clean, and free from oil or grease. 

APPLICATION

By Brush/Roller/Spatula

Apply to one surface in a thin layer, assemble the parts and leave to set, it will set in 30mininutes. During cure this product will expand to fill gaps and rough surfaces, when foamed. Firmly clamp both the substrates. A strong bond will be obtained after 2 - 3 hours and full strength will be realized after 24 hours at room temperature. Individual substrates should be evaluated for bonding performance prior to any large scale application.

CLEAN-UP

Mineral spirit or acetone when glue is wet, sand & scrape when glue is dry

STORAGE

Being a highly reactive moisture curing system, any water contamination of the container will cause problems. Once opened therefore, the glue should be used up as quickly as possible. 

HANDLING

Adhesive is based on diphenyl methane-4, 4-di-isocyanate and is therefore classed as harmful. Wear suitable rubber gloves and eye protective while handling. Keep out of reach of children

SHELF LIFE

Best before nine months from the date of manufacturing in factory sealed container.

PACKING 250g 500 g,